mso-hansi-font-family:"Times New Roman"">一、用途：

mso-hansi-font-family:"Times New Roman"">依据GB/T5480.5-2004 "Times New Roman"">矿物棉及其制品试验方法渣球含量之标准设计制做，可对玻璃棉及其制品，矿渣棉、岩棉、及其制品，硅酸铝棉及其制品进行渣球含量进行分析。具有体积小、外形美观实用等特点，是实验室必备之仪器。

mso-hansi-font-family:"Times New Roman"">二、渣球含量分析测定仪技术参数：

mso-hansi-font-family:"Times New Roman"">玻璃转子流量计：25-250mL/min

mso-hansi-font-family:"Times New Roman"">分离筒：内径80mm "Times New Roman"">；高380mm

mso-hansi-font-family:"Times New Roman"">纤维收集器

mso-hansi-font-family:"Times New Roman"">渣球收集器

mso-hansi-font-family:"Times New Roman"">外形尺寸：310×260×590mm

mso-hansi-font-family:"Times New Roman"">三、渣球含量分析测定仪使用步骤：

1、制备试样

mso-hansi-font-family:"Times New Roman"">按GB/T5480.5-2004 "Times New Roman"">的规定选取式样，切取全厚度的试样11g "Times New Roman"">左右。在对于玻璃棉及其制品，在（500±20 "Times New Roman"">）℃下灼烧30min mso-hansi-font-family:"Times New Roman"">以上；对于硅酸棉及其制品，在（700±20 mso-hansi-font-family:"Times New Roman"">）℃ "Times New Roman"">下灼烧30min "Times New Roman"">以上。除尽粘结剂再称量精确到0.01g "Times New Roman"">。试样数量按产品标准的规定，但不应少于3 "Times New Roman"">个。

2、压制试样

mso-hansi-font-family:"Times New Roman"">把称量好的试样放入相应的试样筒内，放于压榨器上进行手动螺旋加压。

3、润湿试样

mso-hansi-font-family:"Times New Roman"">将压制好的试样取出，放于250mL "Times New Roman"">量杯内，加入表面活性剂溶液50mL "Times New Roman"">，并充分搅拌，使纤维在溶液中得到润湿和分散。

4、分离试验

mso-hansi-font-family:"Times New Roman"">将试样全部移入分离筒中。

mso-hansi-font-family:"Times New Roman"">打开水源开关，使转子流量计的流量示值为60mL/min，保持此流量直至纤维在水中得到分散和悬浮。

mso-hansi-font-family:"Times New Roman"">加大水流量至（120-180 "Times New Roman"">）mL/min "Times New Roman"">，继续分离10min "Times New Roman"">左右。

mso-hansi-font-family:"Times New Roman"">待分离筒内水澄清后，打开分离筒下端的排渣阀，借助水流把渣球完全排入边长不大于产品标准规定的筛孔边长的标准筛内。

mso-hansi-font-family:"Times New Roman"">检查纤维收集器内的纤维中是否含有渣球，若有渣球应将其放入分离器内在进行分离。

mso-hansi-font-family:"Times New Roman"">干燥

mso-hansi-font-family:"Times New Roman"">将盛有渣球的筛子放入电热干燥箱内，在（105-110）℃ mso-hansi-font-family:"Times New Roman"">温度下烘干至少20min "Times New Roman"">。

mso-hansi-font-family:"Times New Roman"">筛分

mso-hansi-font-family:"Times New Roman"">将干燥的渣球移入产品标准规定的筛孔的标准筛内，加入3 mso-hansi-font-family:"Times New Roman"">只直径为（20±1 "Times New Roman"">）mm的陶瓷球，盖装后启动振筛机筛分15min mso-hansi-font-family:"Times New Roman"">。

mso-hansi-font-family:"Times New Roman"">称量

mso-hansi-font-family:"Times New Roman"">将筛分后的渣球放在天平上称重，读数精确到0.01g mso-hansi-font-family:"Times New Roman"">。

mso-hansi-font-family:"Times New Roman"">计算及试验结果

mso-hansi-font-family:"Times New Roman"">计算

mso-hansi-font-family:"Times New Roman"">渣球含量Sh "Times New Roman"">按下式计算：

         Sh=m/mo×100

mso-hansi-font-family:"Times New Roman"">式中：

 Sh— "Times New Roman"">渣球含量，单位为百分数（％）；

m—渣球质量，单位为克（g mso-hansi-font-family:"Times New Roman"">）。

mo-试样质量，单位为克（g mso-hansi-font-family:"Times New Roman"">）。

  "Times New Roman"">试验结果

mso-hansi-font-family:"Times New Roman"">试验结果以算术平均值表示，精确到小数点后第一位。同时报出所有筛孔的孔径。

mso-hansi-font-family:"Times New Roman"">实验完毕后清理好以便下次使用。