品牌:GE
供应:10000公斤
发货:3天内
| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | 15200 | kg/cm2(MPa)[Lb/in2] | |
| 拉伸模量 | ASTM D638/ISO 527 | 7.0 | kg/cm2(MPa)[Lb/in2] | ||
| 拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | 7.0 | % | ||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 60.0 | % | ||
| 弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 60.0 | kg/cm2(MPa)[Lb/in2] | ||
| 弯曲强度 | ASTM D790/ISO 178 | 22000 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | 109 | |||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 0.6 | kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.27 | ||
| 成型收缩率 | ASTM D955 | % | |||
| 熔融指数（流动系数） | 200℃/5kg | ASTM D1238/ISO 1133 | - | g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 | - | g/10min | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.250 | % | ||
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 405 66psi | ℃（℉） |
| 未退火 | ASTM D648/ISO 75 | ℃（℉） | |||
| 维卡软化点 | ASTM D1525/ISO R306 | 426 | ℃（℉） | ||
| 燃烧性（率） | UL94 | V-0 | |||
| 线性膨胀系数 | ASTM D696/ISO 11359 | 3 | mm/mm.℃ | ||
| 电气性能 | 介电常数 | 100HZ | ASTM D150/IEC 60250 | 3.15 | |
| 1MHZ | ASTM D150/IEC 60250 | ||||
| 介电损耗 | 100HZ | ASTM D150/IEC 60250 | |||
| 1MHZ | ASTM D150/IEC 60250 | ||||
| 体积电阻率 | ASTM D257/IEC 60093 | 1E17 | Ω.cm | ||
| 表面电阻率 | ASTM D257/IEC 60093 | Ω | |||
| 耐电弧性 | ASTM D495/IEC 60112 | ||||
| 加工条件 | 干燥条件 | 180°C | 4H | ||
| 加工温度 | 射嘴 | ℃ | |||
| 料筒前段 | 330-340 | ℃ | |||
| 料筒中段 | 330-340 | ℃ | |||
| 料筒后段 | 330-340 | ℃ | |||
| 熔体温度 | ℃ | ||||
| 模具温度 | 50-120 | ℃ | |||
| 压力 | 注塑压力 | 49-98 | Mpa | ||
| 保压压力 | 49-98 | Mpa | |||
| 背压 | 49-98 | Mpa | |||
| 螺杆转速 | rpm | ||||
| 其他 | 备注 | 保压时间5-10 S.冷却时间5-10 S | |||
| 颜色 | 琥珀色（金黄色） | ||||
| 特性 | |||||
| 用途 | 电气，飞机航天，医疗器材,HVAC. | ||||
本公司供应美国GE公司PEI —1010，品牌GE，型号1010。参数为：牌号*1000，产地/厂家*美国，用途级别*FDA和NSF级别，吸水率*0.0250/﹪。质量保证，欢迎咨询洽谈。13829230569